VIZA-Cast Steel Valve-Data Sheet

Data Sheet






...................................................................................................................................................................
	Materials


CHEMICAL COMPOSITIONS (%) max
Material	C	Mn	P	S	Si	Ni	Cr	Mo	Other
WCB	0.30	1.00	0.04	0.045	0.60	0.50	0.50	0.20	Cu 0.30 V 0.03
WC1	0.25	0.50~0.80	0.04	0.045	0.60	0.50	0.35	0.45~0.65	Cu 0.50 W 0.10
WC6	0.05~0.20	0.50~0.80	0.04	0.045	0.60	0.50	1.00~1.50	0.45~0.65	Cu 0.50 W 0.10
WC9	0.05~0.18	0.40~0.70	0.04	0.045	0.60	0.50	2.00~2.75	0.90~1.20	Cu 0.50 W 0.10
C5	0.20	0.40~0.70	0.04	0.045	0.75	0.50	4.00~6.50	0.45~0.65	Cu 0.50 W 0.10
C12	0.20	0.35~0.65	0.04	0.045	1.00	0.50	8.00~10.00	0.90~1.20	Cu 0.50 W 0.10
CA15	0.15	1.00	0.04	0.040	1.50	1.00	11.50~14.00	0.50
LCB	0.30	1.00	0.04	0.045	0.60	0.50	0.50	0.20	Cu 0.30 V 0.03
LCC	0.25	1.20	0.04	0.045	0.60	0.50	0.50	0.20	Cu 0.30 V 0.03
LC2	0.25	0.50~0.80	0.04	0.045	0.60	2.0~3.0
LC3	0.15	0.50~0.80	0.04	0.045	0.60	3.0~4.0
CF8	0.08	1.50	0.040	0.040	2.00	8.0~11.0	18.0~21.0
CF8M	0.08	1.50	0.040	0.040	1.50	9.0~12.0	18.0~21.0	2.0~3.0
CF3	0.03	1.50	0.040	0.040	2.00	8.0~12.0	17.0~21.0	0.50
CF3M	0.03	1.50	0.040	0.040	1.50	9.0~13.0	17.0~21.0	2.0~3.0
CF8C	0.08	1.50	0.040	0.040	2.00	9.0~12.0	18.0~21.0	0.50	Nb =8x C = 1
CN7M	0.07	1.50	0.040	0.040	1.50	27.5~30.5	19.0~22.0	2.0~3.0	Cu 3.0~4.0
A105	0.35	0.60~1.05	0.040	0.050	0.35	0.40	0.30	0.12	Cu 0.40 V0.03 Nb 0.02
F1	0.28	0.60~0.90	0.045	0.045	0.15~0.35			0.44~0.65
F5	0.15	0.30~0.60	0.030	0.030	0.50	0.50	4.0~6.0	0.44~0.65
F11-1	0.05~0.15	0.30~0.60	0.030	0.030	0.50~1.00		1.00~1.50	0.44~0.65
F22-1	0.05~0.15	0.30~0.60	0.040	0.040	0.50		2.00~2.50	0.87~1.13
F6a	0.15	1.00	0.040	0.030	1.00	0.50	11.5~13.5
F304	0.08	2.00	0.040	0.030	1.00	8.0~11.0	18.0~20.0
F304L		2.00	0.040	0.030	1.00	8.0~13.0	18.0~20.0
F316	0.08	2.00	0.040	0.030	1.00	10.0~14.0	16.0~18.0	2.00~ 3.00
F316L	0.035	2.00	0.040	0.030	1.00	10.0~15.0	16.0~18.0	2.00~ 3.00
F321	0.08	2.00	0.040	0.030	1.00	9.0~12.0	= 17.0		Ti =5x C = 0.70
F347	0.08	2.00	0.040	0.030	1.00	9.0~13.0	17.0~20.0		Nb+Ta =10x C =1.10
410	0.15	1.00	0.040	0.030	1.00		11.50~13.50
416	0.15	1.25	0.06	= 0.15	1.00		12.00~14.00
420	Over 0.15	1.00	0.040	0.030	1.00		12.00~14.00
D-2	3.00	0.70~1.25	0.08		1.50~ 3.00	18.00~22.00	1.75~2.75
B7	0.37~0.49	0.65~1.10	0.035	0.040	0.15~ 0.35		0.75~1.20	0.15~ 0.25
B7M	0.37~0.49	0.65~1.10	0.035	0.040	0.15~ 0.35		0.75~1.20	0.15~ 0.25
B16	0.36~0.47	0.45~0.70	0.035	0.040	0.15~ 0.35		0.80~1.15	0.50~ 0.65	V 0.25~0.35
B8	0.08	2.00	0.045	0.030	1.00	8.00~10.50	18.00~20.00
B8M	0.08	2.00	0.045	0.030	1.00	10.00~14.00	16.00~18.00	2.00~ 3.00
L7	0.38~0.48	0.75~1.00	0.035	0.040	0.15~ 0.35		0.80~1.10	0.15~ 0.25
L7M	0.38~0.48	0.75~1.00	0.035	0.040	0.15~ 0.35		0.80~1.10	0.15~ 0.25
B			0.04	0.050
2H	= 0.40	1.00	0.040	0.050	0.40
2HM	= 0.40	1.00	0.040	0.050	0.40
4	0.40~0.50	0.70~0.90	0.035	0.040	0.15~0.35			0.20~ 0.30
7	0.37~0.49	0.65~1.10	0.040	0.040	0.15~0.35		0.75~1.20	0.15~0.25
7M	0.37~0.49	0.65~1.10	0.040	0.040	0.15~0.35		0.75~1.20	0.15~0.25
8	0.08	2.00	0.045	0.030	1.00	8.00~10.50	18.0~20.0
8M	0.08	2.00	0.045	0.030	1.00	10.0~14.0	16.0~18.0	2.00~3.00
.....................................................................................................................................................................................

MECHANICAL PROPERTIES
Material	Tensile,min MPa (ksi)	Yield, min MPa (ksi)	Elongation min (%)	Reduction of Area min (%)	Hardness Brinell
WCB	485~655(70~95)	250 (36)	22	35
WC1	450-620(65-90)	240 (35)	24	35
WC6	485~655(70~95)	275 (40)	20	35
WC9	485~655(70~95)	275 (40)	20	35
C5	620~795(90~115)	415 (60)	18	35
C12	620~795(90~115)	415 (60)	18	35
CA15	620~795(90~115)	450 (65)	18	30
LCB	450-650(65.0-90.0)	240 (35.0)	24	35	J (lbf·ft)18 (13)
LCC	485-655(70.0-95.0)	275 (40.0)	22	35	J (lbf·ft)20 (15)
LC2	485-655(70.0-95.0)	275 (40.0)	24	35	J (lbf·ft)20 (15)
LC3	485-655(70.0-95.0)	275 (40.0)	24	35	J (lbf·ft)20 (15)
CF8	485 (70)	205 (30)	35
CF8M	485 (70)	205 (30)	30
CF3	485 (70)	205 (30)	35
CF3M	485 (70)	205 (30)	30
CF8C	485 (70)	205 (30)	30
CN7M	450 (62)	170 (25)	35
A105	485 (70)	250 (36)	22	30	= 187
F1	485 (70)	275 (40)	20	30	143~192
F5	485 (70)	275 (40)	20	35	143~217
F11-1	415 (60)	205 (30)	20	45	121~174
F22-1	415 (60)	205 (30)	20	35	= 170
F6a	585 (85)	380 (55)	18	35	167~229
F304	515 (75)	205 (30)	30	50
F304L	485 (70)	170 (25)	30	50
F316	515 (75)	205 (30)	30	50
F316L	485 (70)	170 (25)	30	50
F321	515 (75)	205 (30)	30	50
F347	515 (75)	205 (30)	30	50
410	480 (70)	275 (40)	20	45
416					= 262
420					= 241
D-2	400 (58)	207 (30)	8.0		139~202
B7	860 (125)	720 (105)	16	50
B7M	690 (100)	550 (80)	18	50	= HB235 or HRB 99
B16	860 (125)	725 (105)	18	50
B8	515 (75)	205 (30)	30	50	= HB223 or HRB 96
B8M	515 (75)	205 (30)	30	50	= HB223 or HRB 96
L7	860 (125)	725 (105)	16	50
L7M	690 (100)	550 (80)	18	50	= HB235 or HRB 99
B	415~690 (60~100)		18		HRB121~212 HRC 69~95
2H					HB248~352 HRC24~38
2HM					HB159~237 HRC = 22
4					HB248~352 HRC24~38
7					HB248~352 HRC24~38
7M					HB159~237 HRC = 22
8					HB126~300 HRC60~105
8M					HB126~300 HRC60~105
.....................................................................................................................................................................................